Structures by: Merlo F.
Total: 111
Yb Au0.63 Si1.37
Au0.63Si1.37Yb
Zeitschrift fuer Kristallographie (149,1979-) (1999) 214, 108-110
a=4.163Å b=4.163Å c=4.009Å
α=90° β=90° γ=120°
Ca Au1.208 Si0.792
Au1.208CaSi0.792
Zeitschrift fuer Kristallographie (149,1979-) (1999) 214, 108-110
a=4.454Å b=7.139Å c=7.667Å
α=90° β=90° γ=90°
Yb Au1.254 Si0.746
Au1.254Si0.746Yb
Zeitschrift fuer Kristallographie (149,1979-) (1999) 214, 108-110
a=4.431Å b=7.018Å c=7.631Å
α=90° β=90° γ=90°
Ca Au0.64 Si1.36
Au0.64CaSi1.36
Zeitschrift fuer Kristallographie (149,1979-) (1999) 214, 108-110
a=4.151Å b=4.151Å c=4.28Å
α=90° β=90° γ=120°
Yb Au0.88 Si1.12
Au0.88Si1.12Yb
Zeitschrift fuer Kristallographie (149,1979-) (1999) 214, 108-110
a=4.182Å b=4.182Å c=3.962Å
α=90° β=90° γ=120°
AlCo2Gd2
AlCo2Gd2
Zeitschrift fuer Kristallographie (149,1979-) (2002) 217, 415-419
a=4.1016Å b=5.504Å c=8.536Å
α=90° β=90° γ=90°
AlCo2Pr2
AlCo2Pr2
Zeitschrift fuer Kristallographie (149,1979-) (2002) 217, 415-419
a=4.1592Å b=5.573Å c=8.74Å
α=90° β=90° γ=90°
AlCo2Pr2
AlCo2Pr2
Zeitschrift fuer Kristallographie (149,1979-) (2002) 217, 415-419
a=9.595Å b=5.609Å c=7.758Å
α=90° β=103.89° γ=90°
Au2Ca2Pb
Au2Ca2Pb
Zeitschrift für Kristallographie - New Crystal Structures (2001) 216, 1 23-23
a=8.0380(10)Å b=8.0380(10)Å c=3.8254(4)Å
α=90.00° β=90.00° γ=90.00°
Au2PbYb2
Au2PbYb2
Zeitschrift für Kristallographie - New Crystal Structures (2001) 216, 1 24-24
a=8.037(2)Å b=8.037(2)Å c=7.465(2)Å
α=90.00° β=90.00° γ=90.00°
CaLiPb
CaLiPb
Zeitschrift für Kristallographie - New Crystal Structures (2001) 216, 2 173-174
a=4.9330(10)Å b=4.9330(10)Å c=10.9900(10)Å
α=90.00° β=90.00° γ=120.00°